  • Cubic MnFe2O4 particles decorated reduced graphene oxide with excellent microwave absorption properties
  • 来源:疏瑞文教授个人网站 2020-02-23
  • Herein, we have fabricated the reduced graphene oxide/manganese ferrite (RGO/MnFe2O4) hybrid composites by a facile one-pot hydrothermal method. The obtained MnFe2O4 particles exhibited the uniquely cubic morphology with an average particle size of 100.6 nm, which were uniformly attached to the surface of RGO sheets. Results demonstrated that both the ratio of RGO to MnFe2O4 and filling ratio had notable effects on the microwave absorption performance of the as-prepared hybrid composites. Moreover, the hybrid composites showed the characteristics of thin thickness, broad bandwidth and strong absorption. Significantly, the hybrid composite with a filling ratio of 70 wt% (S2) exhibited the best microwave absorption performance, i.e. the minimum reflection loss reached 47.5 dB and effective absorption bandwidth (less than 10 dB) was 5.2 GHz for a thickness of only 1.7 mm. Therefore, the RGO/MnFe2O4 hybrid composites could be potential candidates for application in microwave absorption. 




  • [来源:中国聚合物网]
  • 了解更多请进入: 疏瑞文教授个人网站
相关新闻
  • · Synthesis and high-performance microwave absorption of reduced graphene oxide/zinc ferrite hybrid nanocomposite
  • · Facile preparation and microwave absorption properties of RGO/MWCNTs/ZnFe2O4 hybrid nanocomposites
  • · Fabrication of reduced graphene oxide/multi-walled carbon nanotubes/zinc ferrite hybrid composites as high-performance microwave absorbers
  • · Facile design of nitrogen-doped reduced graphene oxide/zinc ferrite hybrid nanocomposites with excellent microwave absorption in the X-band

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017