  • Effect of crosslinking agent on the properties of low‐temperature curing PES/PTFE anticorrosive coating
  • 来源:关绍巍教授个人网站 2020-03-08
  • To reduce energy consumption and broaden the scope of application of polyethersulfone/polytetrafluoroethylene (PES/PTFE) coatings, three hybrids have been designed by incorporating PES/PTFE coatings with different contents (0, 10, and 20?wt %) of crosslinking agent consisting of epoxy resin and appropriate curing agent (ER‐CA) in the application as low‐temperature curing PES/PTFE coatings and named as EP‐0, EP‐1, and EP‐2, respectively. The addition of ER‐CA gives rise to satisfactory distribution of PTFE, making PTFE play its roles better and improves barrier properties of the coatings by secondary leveling and its own crosslinking structure, which greatly enhances anticorrosion properties. Compared with EP‐0 and EP‐2, EP‐1 exhibits lower water permeability. Even after long‐term exposure to corrosive environments, EP‐1 still possesses high anticorrosion properties.
  • [来源:中国聚合物网]
  • 了解更多请进入: 关绍巍教授个人网站
相关新闻
  • · Synthesis and characterization of crosslinked porphyrin-based polyimides from different terminal alkynyl groups for carbon dioxide adsorption and separation
  • · Porous structure, carbon dioxide capture, and separation in cross-linked porphyrin-based polyimides networks
  • · Crosslinked porphyrin-based polyimides: Tunable porosity parameters and carbon dioxide adsorption
  • · Porphyrin-based porous polyimides: Synthesis, porous structure, carbon dioxide adsorption

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017