  • Low resistance dye-sensitized solar cells based on all-titanium substrates using wires and sheets.
  • 来源:王海教授个人网站 2020-04-26
  • Low resistance dye-sensitized solar cells (DSSCs) based on all-titanium substrates were proposed in this paper. To minimize the internal resistance of DSSCs, the titanium wires and titanium sheets were used as the substrates of the photoanode and the counter electrode, respectively. Compared with the FTO substrate, titanium wires could absorb much diffused light by back reflection since the reflectivity in the titanium sheet was highly increased up to 53.12%. Furthermore, the transmittance of the front cover was increased by 13.2% using the super white glass instead of FTO substrate. The thickness of TiO2 thin film coated on titanium wire was optimized to achieve a high cell performance. The efficiency of 5.6% for the cell was obtained with a Jsc of 15.41 mA cm?2, Voc of 0.59 V, and FF of 0.62. The results showed that the titanium-based DSSCs had superiority for producing the large-scale DSSCs without metal grid line.
  • [来源:中国聚合物网]
  • 了解更多请进入: 王海教授个人网站
相关新闻
  • · MoO3 nanoplates: a high-capacity and long-life anode material for sodium-ion batteries
  • · Unusual improvement of pseudocapacitance of nanocomposite electrodes: Three-dimensional amorphous carbon frameworks triggered by TiO2 nanocrystals
  • · Hydrothermal growth of large-scale macroporous TiO2 nanowires and its application in 3D dye-sensitized solar cells.
  • · An investigation on the novel structure of dye-sensitized solar cell with integrated photoanode