  • Dry–wet spinning of temperature-sensitive PVDF hollow-fiber membranes at different bore fluid flow rates
  • 来源:赵义平教授个人网站 2014-03-10
  • In this work, dry–wet spinning was conducted to fabricate poly(vinylidene fluoride)-g-poly(Nisopropylacrylamide) (PVDF-g-PNIPAAm) copolymer hollow-fiber membranes. The effect of the bore fluid flow rate (BFFR) on the structure and performance of each hollow-fiber membrane was investigated by X-ray photoelectron spectroscopy (XPS), field emission scan electronic microscopy (FESEM), pore-size measurements, mechanical property evaluations, and a filtration experiment. It was found that the grafted PNIPAAm chains aggregated on the inner surface of the fiber membrane due to the effect of the bore fluid. When the permeation temperature was increased from 20 to 45 °C, a drastic reduction in the pure-water flux and a remarkable increase in the retention of bovine serum albumin (BSA) were observed at around32 °C, indicating that the as-prepared fiber membranes exhibit excellent temperature sensitivity. Poresize measurements confirmed that both the mean pore size and the porosity increase with increasing BFFR, endowing the fiber membranes with high pure-water fluxes and low retentions of BSA.
  • [来源:中国聚合物网]
  • 了解更多请进入: 赵义平教授个人网站
相关新闻
  • · Study on the influence of reaction time on the structure and properties of the PVDF membrane modified through the method of atom transfer radical polymerization
  • · Preparation, characterization and application of chiral thermo-sensitive membrane for phenylalanine separation of the racemic mixture
  • · Thermo-responsive Modification and Properties Study of PVDF Flat Membrane
  • · Structure and Performance of Temperature-Sensitive Poly(vinylidene fluoride) Hollow Fiber Membrane Fabricated at Different Take-up Speeds

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017