  • Formation of Breath Figure Arrays in Methanol Vapor Assisted by Surface Active Agents
  • 来源:李磊教授个人网站 2015-03-12
  • Breath figure (BF) process is a promising technique for fabricating honeycomb polymer films. It is usually conducted in water vapor. While, in organic vapors only unique polymer can be used to prepare BF arrays as reported in our previous article (Breath Figure in Nonaqueous Vapor. Sof t Matter, 2013, 506 ?514), although new structure features are induced in the film. In this paper, a universal modified BF processing is devised for preparing porous films in methanol vapor with conventional polymers, by adding a small amount of surface active agent into the casting solution, such as siloxane- and fluorine-containing block copolymers. The pores in the PS films prepared with this method are of
    cylindrical shape with large depth-diameter aspect ratio, and the diameter and depth of pores can be well controlled by the experiment conditions. Based on these results, the formation mechanism of honeycomb structure in methanol vapor is discussed.

  • [来源:中国聚合物网]
  • 了解更多请进入: 李磊教授个人网站
相关新闻
  • · Polymeric nanoporous materials fabricated with supercritical CO2 and CO2-expanded liquids
  • · Electrochemical supercapacitor with polymeric active electrolyte
  • · Mechanism investigation and suppression of self-discharge in active electrolyte enhanced supercapacitors
  • · Directional Photomanipulation of Breath Figure Arrays

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017