  • Fabric electrodes coated with polypyrrole nanorods for flexible supercapacitor application prepared via a reactive self-degraded template
  • 来源:许杰教授个人网站 2015-09-21
  • Wearable energy storage devices that can be used in the garment industry are strongly required to power E-textiles. In this article, polypyrrole (PPy) nanorods were deposited on cotton fabrics via in situ polymerization of pyrrole in the presence of the fibrillar complex of FeCl3 and methyl orange as a reactive self-degraded template. The obtained fabrics could be directly used as supercapacitor electrodes, with a maximum specific capacitance of 325 F g1 and an energy density of 24.7 Wh kg1 at a current density of 0.6 mA cm2. The capacitance remained higher than 200 F g1 after 500 cycles.
  • [来源:中国聚合物网]
  • 了解更多请进入: 许杰教授个人网站
相关新闻
  • · Polypyrrole-coated cotton fabrics prepared by electrochemical polymerization as textile counter electrode for dye-sensitized solar cells
  • · Polypyrrole/reduced graphene oxide coated fabric electrodes for supercapacitor application
  • · Polypyrrole-coated cotton fabrics for flexible supercapacitor electrodes prepared using CuO nanoparticles as template
  • · A flexible polypyrrole-coated fabric counter electrode for dye-sensitized solar cells

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017