  • Preparation and characterization of porous polyelectrolyte complex membranes for nanofiltration
  • 来源:李胜海研究员个人网站 2015-09-25
  • Polyelectrolyte complex membranes were prepared from poly(acrylic acid-co-acrylonitrile)s and imidazolium-based polycations viaa combination of blendfilm casting and ammonia solution immersion procedures. The membranes were free-standing and tough, showing excellent mechanical properties (with tensile strength of 6.71–23.7 MPa and elongation at break of 15–59%). Hierarchically structured nanopores were formed in the membranes during the ammonia soaking step, due to NH3-triggered –COOH deprotonation andin situ ionic crosslinking with polycations. Zeta potential measurements indicated that the membranes were negatively charged under neutral conditions. The membranes exhibited moderate rejection to salts in the order of Na2SO4 > NaCl > MgCl2, but high rejection to methyl orange (>99.9%).
  • [来源:中国聚合物网]
  • 了解更多请进入: 李胜海研究员个人网站
相关新闻
  • · Catechol-functionalized microporous organic polymer as supported media for Pd nanoparticles and its high catalytic activity
  • · Mechanically robust thermally rearranged (TR) polymer membranes with spirobisindane for gas separation
  • · Assembly of an unbalanced charged polyampholyte onto Nafion to produce high-performance composite membranes
  • · Enhancing activity of Suzuki reactions in water by using guanidinium ionic liquid stabilized palladium micelle catalyst

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017