  • Water and salt transport properties of zwitterionic polymers film
  • 来源:孟建强教授,博士生导师个人网站 2016-01-21
  • Two series of crosslinked zwitterionic polymer films were synthesized via UV-photopolymerization of aqueous solution, and the films were prepared using sulfobetaine methacrylate (SBMA) or carboxybetame  methacrylate (CBMA) as  the zwitterionic co-monomer and  polyethylene glycol) diacrylate (PEGDA) as the crosslinker. The water and salt transport properties of the obtained polysulfobetaine methacrylate  (PSBMA)  and  polycarboxybetaine  methacrylate  (PCBMA)  films  were  studied  using permeation and kinetic desorption methods with crosslinked polyethylene glycol) acrylate (PEGA) films as a control. Zwitterionic films absorb more water and are more permeable to both water and salt than PEGA films as a result of interactions between the zwitterions, water molecules, and salt ions. The transport properties of PSBMA and PCSMA depend similarly on crosslinking density, and high water and salt permeability correlates with high water uptake. However, the relationship between salt permeability and salt concentration differed between PSBMA and PCBMA. PSBMA behaves like a charged film, and its salt permeability increases with salt concentration while PCBMA shows the opposite trend.
    Transport properties for both materials are consistent with a trade-off between water permeability and water/salt selectivity. Zwitterionic films exhibit high permeability/low selectivity among polymers reported in the literature. This result suggests that they could be useful as coating materials for membrane fouling control where the anti-fouling properties of the zwitterionic material is more important than water/salt selectivity.
  • [来源:中国聚合物网]
  • 了解更多请进入: 孟建强教授,博士生导师个人网站
相关新闻
  • · Facile scalable synthesis of TiO2/Carbon nanohybrids with ultrasmall TiO2 nanoparticles homogeneously embedded in carbon matrix
  • · A scalable method toward superhydrophilic and underwater superoleophobic PVDF membranes for effective oil/water emulsion separation
  • · Declined ionic flux through the nano-pores of vertically aligned carbon nanotubes filled with PNIPAm hydrogel,
  • · Solvothermal synthesis of hierarchical Eu2O3 nanostructures templated by PS-b-PMAA: morphology control via simple variation of water contents.

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017