  • Photon assisted room-temperature hydrogen sensors using PdO loaded WO3 nanohybrids
  • 来源:张超教授个人网站 2017-01-05
  • In the present paper, we report novel room-temperature hydrogen sensors based on palladium oxide (PdO) loaded tungsten oxide (PdO-WO3) nanohybrids. We synthesized WO3 nanorods by hydrothermal method. Then the as-synthesized nanorods were mixed into PdCl2 solution with a subsequent thermal treatment to form PdO-WO3 nanohybrids. XRD and XPS test confirmed that PdO-WO3 nanohybrids were successfully prepared. FE-SEM and HRTEM images showed that PdO nanoparticles were distributed on the surface of WO3 nanorods in the nanohybrids. UV-Vis spectra indicated that broader visible light absorption range of PdO-WO3 composites was obtained when compared with that of pure WO3. The obtained PdO-WO3 sensors exhibited good responses to ppm-level H2 gas at room temperature under visible light illumination, and the best sensing performance was achieved upon exposure to blue light illumination. The best sensing performance was comparable to the counterpart performed at an elevated temperature between 200 and 250oC.
  • [来源:中国聚合物网]
  • 了解更多请进入: 张超教授个人网站
相关新闻
  • · Preparation and characterization of CuxO1-y@ZnO1-α nanocomposites for enhanced room-temperature NO2 sensing applications
  • · Room-temperature nitrogen -dioxide sensors based on ZnO1?x coatings deposited by solution precursor plasma spray
  • · Sensing properties of Pt/Pd activated tungsten oxide films grown by simultaneous radio-frequency sputtering to reducing gases
  • · Improvement of sensing characteristics of radio-frequency sputtered tungsten oxide films through surface modification by laser irradiation

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017