作者：Cai Zhi-Qi,Sun Jianzhong,Ren Hua,Zhao Qian,Zhou Qiyun
关键字：glass transition, liquid-crystalline polymer, thermosets
论文来源：期刊
具体来源：POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING卷: 47 期: 4 页: 363-366
发表时间：2008年
A novel nanocomposite was prepared by liquid-crystalline epoxy (LCE)/diaminodiphenylsulfone (DDS)/organic montmorillonite (MMT). A novel liquid-crystalline epoxy monomer, diglycidyl ether of 4,4'-bis(4-hydroxylbenzoyloxy)-3,3',5,5'-tetramethylbiphenyl (DGE-BHBTMBP), was chosen as the matrix material. The curing processes and thermal properties of the novel LCETs obtained were investigated by nonisothermal DSC. The peak temperature increased with an increase in the heating rate for the different amount of organic MMT. The exothermal peaks of the samples containing organic MMT shift toward a lower temperature compared with the samples without organic MMT in the same curing condition. The glass transition temperature (T(g)) of cured composites increases as the heat rates decrease.