26. Influence of the existence of a phthalocyanine phase on the dielectric properties of ternary composites: Carbon nanotubes/phthalocyanine/poly(vinylidene fluoride)
作者:Yunhe Zhang, Dan Xu, Wenhan Xu, Weiwei Wei, Shaowei Guan, Zhenhua Jiang
关键字:phthalocyanine,dielectric propertie
论文来源:期刊
具体来源:COMPOSITES SCIENCE AND TECHNOLOGY,2014,104,89-96
发表时间:2014年
Carbon nanotube (CNT)/polymer composites with high dielectric constants are highly desired by the electronic and electric industries. However, high conductivity CNTs exhibit bad dispersion properties in polymers, leading to high dielectric losses in the composites. One effective strategy to overcome these problems involves the fabrication of core-shell structured fillers with CNT cores and non-conductive or semi-conductive shells. In this study, tetra-amido-phthalocyanine copper (4NH(2)-CuPc) coated, acidified multi-walled carbon nanotube (a-MWCNT) composites were fabricated through pi-pi stacking interactions. The coating thickness was controlled by adjusting the concentration of 4NH(2)-CuPc in the mixture and was subsequently confirmed by X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM) analyses. The a-MWCNT5/4NH(2)-CuPc were added to poly(vinylidene fluoride) (PVDF) to produce a-MWCNTs/4NH(2)-CuPc/PVDF composites. The dielectric properties of these composites reached the optimum values when the rate of 4NH(2)-CuPc adsorption on the a-MWCNTs was the highest. A composite with 9 wt% a-MWCNTs and 13.5 wt% 4NH(2)-CuPc (mass ratio a-MWCNT5:4NH(2)-CuPc = 1:1.5) exhibited the largest dielectric constant (3200) and a dielectric loss tangent (2.1 at 1 kHz).