[Compos. Sci. Technol.]Development of wave-transparent, light-weight composites combined with superior dielectric performance and desirable thermal stabilities
作者：Junwei Gu*, Wencai Dong, Shuang Xu, Yusheng Tang, Lin Ye, Jie Kong*
关键字：A. Polymer-matrix composites (PMCs); B. Thermal properties; C. Mechanical
论文来源：期刊
发表时间：2017年
In this paper, a novel interfacial compatibilizer of soluble epoxy-terminated poly (p-phenylene-2, 6-benzobisoxazole) precursor (epoxy-prePBO) was synthesized to modify bisphenol A cyanate ester (BADCy) resin via copolymerization. Compared to PBO fibers/BADCy wave-transparent composites, the obtained PBO fibers/epoxy-prePBO modified BADCy (PBO fibers/PBO-co-BADCy) wave-transparent composite with 7wt% epoxy-prePBO showed ultra-low dielectric constant (ε, 2.68) and dielectric loss tangent (tanδ, 0.0061) values, excellent mechanical properties (flexural strength, 658.5MPa) and interlaminar shear strength (48.4 MPa), and outstanding thermal stability (THeat-resistance index, 262.9oC). These properties proved its potential in applications, such as in radomes and antenna system of aircrafts.
http://dx.doi.org/10.1016/j.compscitech.2017.03.027