Crystal morphology and nonisothermal crystallization kinetics of short carbon Fiber/Poly(trimethylene terephthalate) composites
作者:Run, MT (Run, Mingtao); Song, HZ (Song, Hongzan); Yao, CG (Yao, Chenguang); Wang, YJ (Wang, Yingjin)
关键字:morphology, nonisothermal crystallization
论文来源:期刊
具体来源:JOURNAL OF APPLIED POLYMER SCIENCE
发表时间:2007年
The crystal morphology and nonisothermal crystallization kinetics of short carbon fiber/poly(trimethylene terephthalate) (SCF/PTT) composites were investigated by polarized optical microscopy (POM) and differential scanning calorimetry (DSC). The optical micrographs suggest that the more content of SCF in composites, the smaller size of the spherulites is. Moreover, the addition of SCF can lead to forming banded spherulites in composites. The Avrami equation modified by Jeziorny, Ozawa theory and the method developed by Mo were used, respectively, to fit the primary stage of nonisothermal crystallization of various composites. The results suggest that the SCF served as nucleation agent, accelerates the crystallization rate of the composites, and the more content of SCF, the faster crystallization rate is. Effective activation energy calculated by the differential iso-conversional method developed by Friedman also concludes that the composite with more SCF component has higher crystallization ability than that with less SCF content. The kinetic parameters U* and K-g are determined, respectively, by the HoffmanLauritzen theory.