作者：Yanqin Yang, Qifeng Zhang, Shenghai Li and Suobo Zhang
关键字：porous， polyelectrolyte，membranes， nanofiltration
论文来源：期刊
具体来源：RSC Advances
发表时间：2015年
Polyelectrolyte complex membranes were prepared from poly(acrylic acid-co-acrylonitrile)s and imidazolium-based polycations viaa combination of blendfilm casting and ammonia solution immersion procedures. The membranes were free-standing and tough, showing excellent mechanical properties (with tensile strength of 6.71–23.7 MPa and elongation at break of 15–59%). Hierarchically structured nanopores were formed in the membranes during the ammonia soaking step, due to NH3-triggered –COOH deprotonation andin situ ionic crosslinking with polycations. Zeta potential measurements indicated that the membranes were negatively charged under neutral conditions. The membranes exhibited moderate rejection to salts in the order of Na2SO4 > NaCl > MgCl2, but high rejection to methyl orange (>99.9%).