课题组关于聚苯乙烯磺酸钠改性碳纳米管增强PCL纳米复合材料的学术论文在Polymer Testing上发表。

摘要:Multi-walled carbon nanotubes (MWCNTs) were modified via a non-covalent functionalization technique with poly(sodium 4-styrenesulfonate) (PSS) as the modifier. A well dispersed and stable water dispersion of carbon nanotubes was prepared by ultrasonication of aqueous suspension of MWCNTs in the presence of PSS. Successful wrapping of MWCNTs by PSS was confirmed by High resolution transmission electron microscope (HRTEM). The dispersion was used to fabricate nanocomposites with poly(ε-caprolactone) (PCL) through solution coagulation. Scanning electron microscope (SEM) and transmission electron microscope (TEM) indicate that PSS wrapped MWCNTs dispersed uniformly in PCL matrix without obvious aggregation even with MWCNT loading increased up to 1.0 wt%. Rheological investigation confirmed that rheological network existed in the PCL/MWCNT nanocomposites with the percolation threshold of only 0.3 wt%. The electrical conductivity of the composites was investigated and the results indicate that electrical percolation threshold was also 0.3 wt%. The mechanical properties of PCL were significantly reinforced as evidenced by the improvement in yielding strength, Young''s modulus, and dynamic storage modulus with incorporation of PSS wrapped MWCNTs.


链接:http://www.sciencedirect.com/science/article/pii/S0142941816300095

Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号