Study on Rheological Behavior of PBT-Clay Nanocomposites. European Polymer Journal, 2005, 41, 2199-2207.
来源:吴德峰教授个人网站 发布日期:2009-09-11
作者:Defeng Wu, Chixing Zhou, Hong Zheng, Dalian Mao, Bian Zhang.
关键字:rheology; PBT; clay; nanocomposites.
论文来源:期刊
具体来源:European Polymer Journal
发表时间:2005年

European Polymer Journal

ABSTRACT: Poly(butylene terephthalate)/montmorillonite composites (PBT/MMT) were prepared by melt intercalation and then investigated using X-ray diffractometer (XRD) and transmission electron microscope (TEM) as well as parallel plate rheometer. It was found that the composites had various phase morphologies with nano-scales and distinct behaviors of a percolation network structure under certain conditions. The linear viscoelastic region of the composites is much narrower than that for PBT matrix, the percolation threshold of the composites is near 3wt%, and the percolation network structure is not stable under a shear as well as in a quiescent annealing process. Moreover, PBT/MMT presents the nature of temperature independence of  versus  whether the internal percolated tactoids network formed or not. The magnitudes of the stress overshoots observed in the reverse flow experiments were strongly dependent on the rest time, which could be inferred that the ruptured network is reorganized under the quiescent annealing process. Furthermore, PBT/MMT shows a strain-scaling stress response to the startup of steady shear, indicating that the formation of the liquid crystalline-like phase structure in the nanocomposites may be the major drive force for the reorganization of the internal network.

Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号