【Adv Funct Mater】Direct 3D Printed Biomimetic Scaffolds Based on Hydrogel Microparticles for Cell Spheroid Growth
来源:付俊教授个人网站 发布日期:2020-12-28
作者:Hua Zhang, Yang Cong, Amarachi Rosemary Osi, Yang Zhou, Jun Fu* et al.
关键字:3D printing, biomimetic scaffolds, hydrogel microparticles, cell spheroid
论文来源:期刊
具体来源:Advanced Functionial Materials
发表时间:2020年
Biocompatible hydrogel inks with shear‐thinning, appropriate yield strength, and fast self‐healing are desired for 3D bioprinting. However, the lack of ideal 3D bioprinting inks with outstanding printability and high structural fidelity, as well as cell‐compatibility, has hindered the progress of extrusion‐based 3D bioprinting for tissue engineering. In this study, novel self‐healable pre‐cross‐linked hydrogel microparticles (pcHμPs) of chitosan methacrylate (CHMA) and polyvinyl alcohol (PVA) hybrid hydrogels are developed and used as bioinks for extrusion‐based 3D printing of scaffolds with high fidelity and biocompatibility. The pcHμPs display excellent shear thinning when injected through a syringe and subsequently self‐heal into gels as shear forces are removed. Numerical simulations indicate that the pcHμPs experience a plug flow in the nozzle with minimal disturbance, which favors a steady and continuous printing. Moreover, the pcHμPs show a self‐supportive yield strength (540 Pa), which is critical for the fidelity of printed constructs. A series of biomimetic constructs with very high aspect ratio and delicate fine structures are directly printed by using the pcHμP ink. The 3D printed scaffolds support the growth of bone‐marrow‐derived mesenchymal stem cells and formation of cell spheroids, which are most important for tissue engineering.
Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号