Preparation of polypropylene/carbon nanotube composite powder with a solid-state mechanochemical pulverization process
来源:李侃社教授个人网站 发布日期:2010-09-21
作者:Xia, Hesheng; Wang, Qi; Li, Kanshe; Hu, Guo-Hua
关键字:Polypropylenes; Carbon nanotubes; Comminution; Crystallization; Micrometers; Adhesion; Dispersions
论文来源:期刊
具体来源:Journal of Applied Polymer Science,2004,93 (1):378-386
发表时间:2004年

A solid-state mechanochemical pulverization process, that is, pan milling, was used to prepare a polypropylene (PP)/carbon nanotube (CNT) composite powder. The composite powder was then melt-mixed with a twin-roll masticator to obtain a PP/CNT composite. The morphology of the PP/CNT powder and the PP/CNT composite was investigated. The crystallization and mechanical properties of the latter were also studied. After 20 milling cycles (ca. 60 min), the average diameter of PP/3 wt % CNT composite powder particles was a few micrometers. The length of the CNTs was reduced from a few micrometers to 0.4-0.5 μm. The CNTs became straighter and more uniform in length. The effects of incorporating the CNTs into PP were as follows: (1) the crystallization rate and temperature of PP increased, (2) a strong b-plane orientation of PP was induced, and (3) the Young's modulus and yield strength of PP increased. Interfacial adhesion between PP and the CNTs was improved by the mechanical action of the solid-state pulverization process used, which favored the dispersion of the CNTs into PP.

Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号