140. Facile Fabrication of Magnetite Microtubes from Electrospun Fiber Template.
来源:刘天西教授个人网站 发布日期:2011-05-12
作者:R.Y.Wang, D.Chen, L.L.Ren, J.Guo, T.X.Liu*
关键字:Electrospun Polystyrene Fibers, Template, Magnetite Microtubes
论文来源:期刊
具体来源:J. Mater. Res., 2011, 26(9), 1072-1075.
发表时间:2011年

The preparation and characterization of Fe3O4 microtubes by a polymer-based template approach were described. Fe3O4 tubes with diameter of 600-650 nm and an average tube thickness of about 50 nm were fabricated after removing the electrospun polystyrene fiber template. The microtubes were composed of individual Fe3O4 nanocrystals. The synthesis process was ambient, generalizable, inexpensive, and nontoxic. The magnetite tubes thus fabricated behave with a saturation magnetization of 37 emu/g measured in the vibrating sample magnetometer. The microtubes prepared in this way might find potential applications in catalysis, magnetic fluid, and biological field.

Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号