Fabrication of reduced graphene oxide/multi-walled carbon nanotubes/zinc ferrite hybrid composites as high-performance microwave absorbers
作者:Ruiwen Shu*, Gengyuan Zhang, Jiabin Zhang, Xin Wang, Meng Wang, Ying Gan, Jianjun Shi, Jie He
关键字:Reduced graphene oxide, Zinc ferrite, Hybrid composite, Solvothermal, Microwave absorption
论文来源:期刊
具体来源:Journal of Alloys and Compounds
发表时间:2018年

Reduced graphene oxide/multi-walled carbon nanotubes/zinc ferrite (RGO/MWCNTs/ZnFe2O4) hybrid composite was fabricated by a facile solvothermal route. The structure, morphology and magnetic properties of the as-prepared composite have been investigated. It was found that the MWCNTs twisted around ZnFe2O4 microspheres and interlinked with RGO, which resulting in the highly connected threedimensional conductive networks were observed in the ternary composite. Moreover, the ternary composite exhibited excellent microwave absorption performance with the minimum reflection loss of 22.2 dB and maximum absorption bandwidth (less than 10 dB) of 2.3 GHz for a thickness of only 1.0 mm. Besides, the microwave absorption mechanism of the composite was also explored. These results indicated that the RGO/MWCNTs/ZnFe2O4 composite was an ideal candidate to be used as microwave absorbers with lightweight, high-efficient performance and thin thickness.