Functionalization of Graphene and Its Influence on Mechanical Properties and Flame Retardancy of Jute/Poly(lactic acid) Composite
作者:Yu T, Hu CQ, Li Y
关键字:Nanocomposites; Graphene; Jute; Poly(lactic acid); Flame Retardancy
论文来源:期刊
具体来源:Journal of Nanoscience and Nanotechnology
发表时间:2019年
In this work, 9,10-dihydro-9-oxa-phosphaphenanthrene-10-oxide (DOPO) was covalently grafted onto the surface of graphene to get modified graphene (G-DOPO) firstly. The mechanical properties and flame retardancy of jute/poly(lactic acid) (PLA) composite with G-DOPO were studied. According to Fourier transform infrared (FTIR) spectroscopy, Raman spectroscopy, and X-ray photoelectron spectroscopy (XPS), it was confirmed that DOPO was grafted on the surface of graphene successfully. Thermogravimetric analysis (TGA) results demonstrated that the residue char of the composites increased with the addition of G-DOPO. The total heat release (THR) of the composite was significantly reduced and the limiting oxygen index (LOI) increased after adding G-DOPO into the composite. Moreover, the mechanical properties results showed that the comprehensive effects of G-DOPO on the interface enhancement and matrix toughness were found.