作者：Gang Huang, Huanhuan Zhang, Yulin Liu, H. J. Chang, H. W. Zhang, H.Z. Song, Donghua Xu*, T.F. Shi*
关键字：///
论文来源：期刊
具体来源：Macromolecules 2017, 50, 2124-2135.
发表时间：2017年

The large-amplitude oscillatory shear (LAOS) behavior of poly(vinyl alcohol) (PVA)/borate hydrogels was investigated with the change of scanning frequency (ω) as well as concentrations of borate and PVA. The different types (Types I?IV) of LAOS behavior are successfully classified by the mean number of elastically active subchains per PVA chain ( feas) and Deborah number (De = ωτ, τ is the relaxation time of sample). For the samples with Type I behavior (both storage modulus G′ and loss modulus G″ increase with strain amplitude γ, i.e., intercycle strain hardening), the critical value of strain amplitude (γcrit) at the onset of intercycle strain hardening is almost the same when De > ～2 (Region 3), while the value of Weissenberg number (Wi = γDe) at γcrit is similar when De < ～0.2 (Region 1). For intracycle behavior in the Lissajous curve, intracycle strain hardening is only observed in viscous Lissajous curve of Region 1 or in the elastic Lissajous curve of Region 3. In Region 1, both intercycle and intracycle strain hardening are mainly caused by the strain rate-induced increase in the number of elastically active chains, while non-Gaussian stretching of polymer chains starts to contribute as Wi > 1. In Region 3, strain-induced non-Gaussian stretching of polymer chains results in both intercycle and intracycle strain hardening. In Region 2 (～0.2 < De < ～2), two involved mechanisms both contribute to intercycle strain hardening. Furthermore, by analyzing the influence of characteristic value of De as 1 on the rheological behavior of PVA/borate hydrogels, it is concluded that intercycle strain hardening is dominated by strain-rate-induced increase in the number of elastically active chains when De < 1, while straininduced non-Gaussian stretching dominates when De > 1.