Click-chemistry approach for graphene modification: effective reinforcement of UV-curable functionalized graphene/polyurethane acrylate nanocomposites
作者:Bin Yu, Yongqian Shi, Bihe Yuan, Lu Liu, Hongyu Yang, Qilong Tai, Siuming Lo, Lei Song, Yuan Hu*,
关键字:Click-chemistry,graphene modification,polyurethane acrylate
论文来源:期刊
具体来源:Rsc Advances
发表时间:2015年
This work presents an effective method of preparing graphene reinforced UV-curable materials. Octamercaptopropyl polyhedral oligomeric silsesquioxane (OMP-POSS) functionalized reduced graphene oxide (FRGO) was prepared through a thiol-ene click approach and the FRGO/polyurethane acrylate (PUA) nanocomposite was fabricated by UV irradiation technology. The results of transmission electron microscopy and X-ray photoelectron spectroscopy indicated that OMP-POSS was successfully grafted onto the surface of graphene nanosheets. Thermal and mechanical properties were investigated by thermogravimetric analysis and dynamic mechanical analysis, respectively. The initial degradation temperature, storage modulus at -65 degrees C and glass transition temperature of FRGO/PUA1.0 nanocomposite were remarkably improved by 12 degrees C, 57.8% and 10 degrees C, respectively, compared to those of neat PUA. Those significant enhancements were attributed to the good dispersion of the nanofiller and the strong interfacial interactions between FRGO and PUA matrix.