Super‐tough poly(lactic acid) using a fully bio‐based polyester containing malic acid via in‐situ interfacial compatibilization
作者：Yang, Rong Cao, Hongwei Li, Chong Zou, Guoxiang Zhang, Xin Li, Jinchun
关键字：biopolymers and renewable polymers, blends, compatibilization, morphology
论文来源：期刊
具体来源：Journal of Applied Polymer Science
发表时间：2021年
Reactive interfacial compatibilization is the most efficient way to prepare super-tough poly (lactic acid) (PLA) materials. Introducing a post-reactive group into a toughening agent that can react with PLA is the key issue. Herein, we reported a series of fully bio-based polyesters (PBSePM) synthesized with sebacic acid, diethyl malate, 1,3-propanediol, and 1,4-butanediol via transesterification in one pot. Super-tough PLA materials can be obtained by reactively blending with PBSePM in the presence of hexamethylene diisocyanate (HDI). In the processing, the side hydroxyl group of the PBSePM reacted with HDI and formed polyurethane elastomer to improve the toughness of PLA. Moreover, the in-situ formed PLA-g-PBSePM grafted copolymer enhanced the interfacial adhesion. With increasing diethyl malate moiety in PBSePM, the PBSePM phase morphology transformed from co-continuous phase structure to semi-continuous and “sea-island” phase structure. When adding 20 wt% PBSePM, all PLA/PBSePM blends have a notched impact strength higher than 53 kJ m2, suggested a super toughness effect. Maximum impact strength of 83 kJ m2 was realized while the PBSePM containing 20% diethyl malate moiety. In addition, super-tough PLA materials can be achieved by only adding 15 wt% PBSePM20, exhibited a highly efficient toughening effect.