A Morphology Study of Poly(divinylbenzene-co-acrylic acid) in Precipitation Polymerization
作者:Feng Bai, Xinlin Yang*, Wenqiang Huang*
关键字:Precipitation-Polymerization; Divinylbenzene; Acrylic acid; Morphology; Solvent effect; Hydrogen bonding
论文来源:期刊
具体来源:1) Chin. J. Polym. Sci., 24(2), 163-171 (2006).
发表时间:2006年
Divinylbenzene-80 (DVB-80) and polar monomer acrylic acid (AA) having hydrogen bonding at a total monomer loading of 5 vol% were precipitated-copolymerized in a variety of organic solvents with 2,2′-azobis(isobutyronitrile) (AIBN) as initiator. The experiments were investigated from a two-dimensional matrix, i.e., the actual crosslinking degree of DVB varying from 0 to 80% and the solvent composition varying from 0 to 100% of toluene mixture with acetonitrile, when the mixture of acetonitrile and toluene was used as the reaction solvent. Under various reaction conditions, six distinct
morphologies including soluble polymers, swellable microgels, coagulum, irregular microparticles, and nano-/micrometer microspheres were formed and the structures of these polymer architectures were described. A morphological map was utilized to discuss the effects of both crosslinking degree of DVB and composition of solvent on the transitions between morphology domains. The results demonstrated that the microspheres are formed by an internal contraction due to the marginal solvency of the continuous phase and the crosslinking of the polymer network through the covalent bonding from DVB as well as the interchain hydrogen-bonding between the carboxylic acid units.