作者：Wu, Defeng*，Shi, Tiejun，Yang, Tao，Sun, Yurong，Zhai, Linfeng，Zhou, Weidong，Zhang, Ming，Zhang, Jie
关键字：Poly(trimethylene terephthalate)， Carbon nanotubes， Composites，Rheology，Electrospinning
论文来源：期刊
具体来源：European Polymer Journal
发表时间：2011年
Poly(trimethylene terephthalate) (PTT) nanocomposites containing carbon nanotubes (CNTs) with different surface structure and aspect ratio were prepared by melt compounding for electrospinning. The dispersion state of the CNTs in the composites was then examined utilizing rheology tools. The results show that carboxylic surface functionalized CNTs present better dispersion in the matrix than hydroxy surface functionalized CNTs because the former has stronger affinity to the PTT. Besides surface functionalization, the aspect ratio of CNTs is also vital to their final dispersion. The CNTs with lower aspect ratio are dispersed as individuals or small bundles while those with higher aspect ratio are dispersed mainly as flocs with large hydrodynamic radius, showing higher effective volume fraction. The presence of CNTs has a large influence on the morphologies of electrospun fiber and on the appearances of CNTs in the fibers. In the presence of CNTs with lower aspect ratio, continuous composite fibers are obtained. But the structure of those continuous fibers highly depends on the surface group of CNTs. Carboxylic surface functionalized CNTs are well embedded by the PTT and oriented along the fiber axis during electrospinning, leading to bead-free and uniform fiber morphology; while hydroxy surface functionalized CNTs show tortuous conformations with less orientation in the fibers, and as a result, the obtained fibers show beaded and misshaped morphologies. In the case of higher aspect ratio, however, the CNTs prefer to exist as entanglements or knots in the streamlines, and thereby only beaded or even uncontinuous fibers are obtained. Therefore, the formation and fiber morphology of PTT/CNT composite fibers obtained by electrospinning strongly depend on the surface functional groups of the CNTs, as well as on the CNT structure.