作者：Zhang, YC，Wang, GL，Li, KW，Zhang, M，Hu, XY，Wang, H
关键字：A1. Characterization; A1. Crystallites; Al. X-ray diffraction; A2. Industrial crystallization; B1. Oxides; B1. Perovskite
论文来源：期刊
具体来源：Journal of Crystal Growth
发表时间：2006年
Uniform, submicron BaTiO₃ crystallites in tetragonal structure were synthesized by a novel low-temperature liquid–solid reaction method mainly via two simple steps: firstly, BaO₂·H₂O₂ submicron particles of about 130–450 nm were precipitated from the reaction of BaCl₂ and H₂O₂ in a slightly alkaline (pH 8) aqueous solution under the ambient condition; secondly, tetragonal phase BaTiO₃ submicrocrystals with the size in the range of 180 to 400 nm could be produced by subjecting the as-prepared BaO₂·H₂O₂ and commercial TiO₂submicron particles to thermal treatment in air at 700 °C for 10 h. The as-obtained products were characterized by X-ray powder diffraction, Raman spectroscopy, Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy and inductively coupled plasma-atomic emission spectroscopy, and scanning electron microscopy.