Intercalation of phosphotungstic acid into layered double hydroxides by reconstruction method and its application in intumescent flame retardant poly (lactic acid) composites
作者:Zhang, Sheng;Yan, Yongxin;Wang, Wenjia;Gu, Xiaoyu,Li, Hongfei, Li, Jianhua,Sun, Jun*
关键字:Polymer Degradation and Stability
论文来源:期刊
具体来源:Poly (lactic acid)Phosphotungstic acidLayered double hydroxidesFlame retardancy
发表时间:2018年
Phosphotungstic acid is a typical kind of superior catalysts, and it is hardly to intercalate into the layered double hydroxides (LDH) by ion-exchange process because of its low negative charge. In this work, a phosphotungstic acid intercalated MgAl-LDH (PWA-LDH) was prepared by reconstruction method, and it was then introduced into poly (lactic acid) (PLA) resin in association with intumescent flame retardant (IFR) by melt blending to prepare a flame-retardant biodegradable PLA composite. The effects of PWA-LDH on the flame retardancy of PLA composites were characterized by limiting oxygen index (LOI), vertical burning test (UL-94) and cone calorimeter test. The results showed that the composite sample containing 18.0 wt% IFR and 2.0 wt% PWA-LDH achieved the maximal LOI value of 48.3%, passed the UL-94 V-0 rating, and significantly decreased the peak heat release rate from 306.3 kW/m2 of neat PLA to 40.1 kW/m2. Thermogravimetric analysis showed that both the thermal stability and the char formation were enhanced. The char morphology observation revealed that PWA-LDH was beneficial to form dense and compact char layers. It was demonstrated that there existed a synergistic effect between IFR and PWA-LDH in promoting the char formation and enhancing the fire resistance.