作者：Pengcheng Wang,Fengzhu Li,Ke-Jian Jiang, Haochen Fan,Yue Zhang, Xueqin Zhou, YanLin Song et al
关键字：crystal growth, ion exchange/insertion reaction, lead-free perovskites, solar cell
论文来源：期刊
具体来源：Advanced Science
发表时间：2020年
The low toxicity, narrow bandgaps, and high charge-carrier mobilities make tin perovskites the most promising light absorbers for low-cost perovskite solar cells (PSCs). However, the development of the Sn-based PSCs is seriously hampered by the critical issues of poor stability and low power conversion efficiency (PCE) due to the facile oxidation of Sn2+ to Sn4+ and poor film formability of the perovskite films. Herein, a synthetic strategy is developed for the fabrication of methylammonium tin iodide (MASnI3) film via ion exchange/insertion reactions between solid-state SnF2 and gaseous methylammonium iodide. In this way, the nucleation and crystallization of MASnI3 can be well controlled, and a highly uniform pinhole-free MASnI3 perovskite film is obtained. More importantly, the detrimental oxidation can be effectively suppressed in the resulting MASnI3 film due to the presence of a large amount of remaining SnF2. This high-quality perovskite film enables the realization of a PCE of 7.78%, which is among the highest values reported for the MASnI3-based solar cells. Moreover, the MASnI3 solar cells exhibit high reproducibility and good stability. This method provides new opportunities for the fabrication of low-cost and lead-free tin-based halide perovskite solar cells.