  • Tailoring the chemical composition and dispersion behavior of fluorinated graphene oxide via CF4 plasma
  • 来源:徐志伟教授个人网站 2015-12-30
  • Grafting fluorine onto graphene oxide (GO) by CF4 plasma treatment was investigated in this study. An easy, low-cost, and effective synthesis of the high-dispersive fluorinated GO (FGO) with tunable atomic ratio of F/O (RF/O) has been realized and the RF/O can be readily manipulated just by adjusting the reaction time. The influence of plasma treatment time on the microstructure, morphology, and dispersion of graphene nanosheets was systematically analyzed. X-ray photoelectron spectroscopy analysis confirmed that fluorine has been grafted onto graphene, and the RF/O was gradually increased to 3.54 for the FGO treated for 20 min. Morphology investigation indicated that etching on the edge of GO occurred during the fluorination. The dispersion performance of FGO in water reduced continuously, which in N,N-dimethylacetamide (DMAc) increased firstly and then decreased with the increase in plasma time. The zeta potentials of FGO in DMAc reached the lowest at ?28.6 mV when GO was treated for 10 min. The dispersion of FGO in water should be attributed to the decrease of C–O group, while there was a same variation trend of FGO zeta potential in DMAc as the value of C–F content, regardless of RF/O, CF2 group content and CF3 group content. The GO film was super-hydrophilic and the film of FGO treated for 20 min was found to be neither hydrophilic nor hydrophobic.
  • [来源:中国聚合物网]
  • 了解更多请进入: 徐志伟教授个人网站
相关新闻
  • · Assembly of graphene oxide on nonconductive nonwovens by the synergistic effect of interception and electrophoresis
  • · Superior Mechanical Properties of Epoxy Composites Reinforced by 3D Interconnected Graphene Skeleton
  • · Optimization of interfacial microstructure and mechanical properties of carbon fiber/epoxy composites via carbon nanotube sizing
  • · Switchable hydrophobic/hydrophilic surface of electrospun poly (l-lactide) membranes obtained by CF4 microwave plasma treatment

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017