  • Switchable hydrophobic/hydrophilic surface of electrospun poly (l-lactide) membranes obtained by CF4 microwave plasma treatment
  • 来源:徐志伟教授个人网站 2015-12-30
  • A switchable surface that promotes either hydrophobic or hydrophilic wettability of poly (l-lactide) (PLLA) microfibrous membranes is obtained by CF4 microwave plasma treatment in this paper. The results indicated that both etching and grafting process occurred during the CF4 plasma treatment and these two factors synergistically affected the final surface wettability of PLLA membranes. When plasma treatment was taken under a relatively low power, the surface wettability of PLLA membranes turned from hydrophobic to hydrophilic. Especially when CF4 plasma treatment was taken under 100 W for 10 min and 150 W for 5 min, the water contact angle sharply decreased from 116 ± 3.0° to ~0°. According to Field-emission scanning electron microscopy (FESEM) results, the PLLA fibers were notably etched by CF4 plasma treatment. Combined with the X-ray photoelectron spectroscopy (XPS) measurements, only a few fluorine-containing groups were grafted onto the surface, so the etching effect directly affected the surface wettability of PLLA membranes in low plasma power condition. However, with the plasma power increasing to 200 W, the PLLA membrane surface turned to hydrophobic again. In contrast, the morphology changes of PLLA fiber surfaces were not obvious while a large number of fluorine-containing groups grafted onto the surface. So the grafting effect gradually became the major factor for the final surface wettability.
  • [来源:中国聚合物网]
  • 了解更多请进入: 徐志伟教授个人网站
相关新闻
  • · Assembly of graphene oxide on nonconductive nonwovens by the synergistic effect of interception and electrophoresis
  • · Superior Mechanical Properties of Epoxy Composites Reinforced by 3D Interconnected Graphene Skeleton
  • · Optimization of interfacial microstructure and mechanical properties of carbon fiber/epoxy composites via carbon nanotube sizing
  • · Tailoring the chemical composition and dispersion behavior of fluorinated graphene oxide via CF4 plasma

关于我们  |  联系我们  

网站:中国聚合物网

polymer.cn Copyright ©2017