交替层状PP/β-PP材料中|3横晶的制备与形态研究
等规聚丙烯( iPP)由于其自身低廉的价格和各项优异的性能而得到广泛应用。聚丙烯主要有三种晶型：α晶，β晶和γ晶；其中，β晶由于其优异的韧性而得到广泛研究[1]。通常，制备高含量β晶聚丙烯最简单有效的方法是通过外加β成核剂。关于聚丙烯β晶的研究主要集中在对β球晶的研究，对β横晶研究较少;而β横晶相关研究又主要研究纤维诱导β横晶[2]，纤维诱导的β横晶主要产生在纤维表面是一维的且少量的，这就阻碍了对p横晶潜在...
http://www.polymer.cn/research/dis_info18719 |
| |
Effects of jute fiber pretreatments on mechanical properties of jute/PP composite
关键字：jute/PP composite,jute fiber pretreatments,mechanical properties,surface analysis
In this study, jute fiber was pretreated by sodium hydroxide, acetic acid and silane coupling agent (KH550). Linear density, moisture absorption, mechanical properties, FTIR analysis and SEM morphology observation of jute fibers were t...
http://www.polymer.cn/research/dis_info11529 |
| |
PP/LDH nanocomposites via melt-intercalation: synergistic flame retardant effects, properties, and applications in automobile industries
关键字：LDH; PP; Nanocomposites; Flame retardant; Application
The structure, thermal behavior and flame retardant properties ofpolypropylene (PP) nanocomposites treated with complex flame retardants composedof layered double hydroxides (LDH) and ammonium polyphosphate(APP)/pentaerythritol (PER) intumescent flame retardant&nbs...
http://www.polymer.cn/research/dis_info11167 |
| |
表面等离子体改性增容PP/PS合金研究
关键字：PP/PS合金
等离子体可分为高温等离子体和低温等离子体[1]，低温等离子体又称为非平衡等离子体。由辉光放电和无声放电（介质阻挡放电）可得到低温等离子体，用低温等离子体使惰性聚合物表面活化能够形成多种化学反应。当使用非聚合反应气体，如氩气和氦气处理聚合物表面时，能够产生活性集团与空气中氧和水反应，进而能形成接枝聚合单体，如丙烯酸，得到亲水的表面或交联层。聚合物表面的等离子体修饰或改性十分广泛。因此，有大量的研究和应...
http://www.polymer.cn/research/dis_info11065 |
| |
微孔发泡PP材料的变形断裂行为研究
关键字：：microcellar PP fracture
The microcellar foamed PP was made via the method of twice-opening molding had uniformly-distributed cells with diameters between 30μm and 50μm. Compared with PP, the density of microcellular foamed PP was reduced about 15%, the...
http://www.polymer.cn/research/dis_info8164 |
| |
PP/Mg(OH)2/EG复合材料的燃烧行为研究
关键字：PP EG MH 阻燃
本文主要研究了EG与MH在阻燃PP时的协同效应。
http://www.polymer.cn/research/dis_info8052 |
| |
TLCP及纳米CaCO3增强改性PP的研究
关键字：TLCP 纳米CaCO3 改性 PP
本文利用原位复合技术，将热致液晶高分子（TLCP）作为增强剂与PP进行原位复合，充分利用液晶高分子的链刚性、高长径比、高模量、高强度和高耐热性等特性，就地形成微纤并分散在基体中，从而提高PP的力学性能，同时改善PP塑料的流变性能和加工性能；利用纳米CaCO3对PP进行增韧改性，且降低TLCP增强PP原位复合材料的各向异性，同时减少增强增韧PP复合材料的成本。
http://www.polymer.cn/research/dis_info7962 |
| |
FEM SIMULATION OF INTERFACIAL STRESS IN TENSILE OF PP-GLASS PARTICLES AND PP-RUBBER BLENDS
关键字：FEM,SIMULATION,INTERFACIAL,STRESS,TENSILE,GLASS,PARTICLES,AND,RUBBER,BLENDS,
Polypropylene (PP) is usually reinforced with glass particles and toughened with rubber,and furthermore the mechanical properties of composites are directly affected by the interfacial stress and its distribution.
http://www.polymer.cn/research/dis_info5530 |
| |
低硬度NBR/PP TPV 的制备与研究
关键字：增塑剂；DOP；NBR；PP；TPV
研究了增塑剂DOP 对共混型NBR/PP TPV 的增塑效果。对增塑后的共混物分别进行了力学性能、流动性能以及老化性能的研究。结果表明，DOP 对NBR/PP 共混体系的增塑效果非常明显，能在很大程度上降低其硬度，并且共混物的流动性能及老化性能也非常优越，但是其耐抽出性不是很好，故用作耐油制品时，DOP 用量不宜过大。
http://www.polymer.cn/research/dis_info4664 |
| |
水镁石/ nano CaCO3/EPDM/PP的性能研究
关键字：nano CaCO3，MH-KH570，EPDM，PP
水镁石其主要成分为氢氧化镁，是自然界存在的含镁最高的矿物。将水镁石超细粉碎到一定细度后再经过适当的表面改性处理可制成低烟、无卤、环境友好的高性能阻燃填料，是我国阻燃材料当前和末来的主要发展方向之一。但是，要达到较好的阻燃效果，水镁石粉阻燃剂的用需量要大；粒度太粗的阻燃填料，在聚合物中大比例的填充将降低聚合物基复合材料的力学性能。为此，必须要对其进行超细粉碎加土，同时通过适当的表面改性提高其与高聚物...
http://www.polymer.cn/research/dis_info3715 |
| |