Influence of the microstructures of porous electrospun poly-(lactic-co-glycolic acid)/carbon nanotubes composite nanofibers and macroporous films on the growth of fibroblast cells
关键字：poly(lactic-co-glycolic acid),Multi-walled carbon nanotubes,nanofibers,macroporous films
Porous polymer nanofibers and macroporous polymer membranes have been generally used as tissue engineering scaffolds. However, the effect of the microstructures related to different porous materials on the cell growth and proliferation rema...
http://www.polymer.cn/research/dis_info11572 |
| |
无定形B-Co合金包覆对尖晶石钴铁氧体电磁性能的影响
关键字：spinel cobalt ferrite,b-co alloy,electromagnetic properties,complex permeability,complex permittivity
Amorphous B-Co alloy has been successfully coated on the co-precipitation synthesized CoFe2O4 fine particles by chemicalreduction. The complex permeability and complex permittivity of the prepared samples have been investigated in the frequency&...
http://www.polymer.cn/research/dis_info7030 |
| |
WC-20%Co 复合粉的制备及其放电等离子烧结的研究
关键字：WC-20%Co 复合粉,原位反应,高钴硬质合金,板状晶
利用放电等离子烧结技术将WO3、Co3O4 和碳黑的高能球磨混合粉经真空还原碳化后合成的WC-20%（质量分数）Co 复合粉烧结为致密的高钴WC-Co 硬质合金材料。研究了制备复合粉的工艺和放电等离子烧结过程以及制备合金的相组成、显微组织、物理和力学性能。实验表明，高能球磨粉在真空条件下原位还原碳化反应得到物相纯净的超细复合粉，此后复合粉在1190～1210℃SPS 烧结成致密块体材料。通过SEM 观察发现，由...
http://www.polymer.cn/research/dis_info6180 |
| |
原位乳液聚合法制备P(MMA-co-AN)/TiO2复合粒子
关键字：有机/无机复合，P(MMA-co-AN)/TiO2 复合粒子，乳液聚合，光催化
有机/无机复合高分子材料兼具有机物和无机物两种材料的性能，应用广泛。通过原位乳液聚合法制备有机/无机复合粒子可以使无机粉体更好的分散在聚合物中，同时又能获得较高的聚合物接枝效率。基于TiO2 优良的光催化活性但却易于团聚，光催化效率不高的问题，本文提出通过原位乳液聚合法制备聚（甲基丙烯酸甲酯-co-丙烯腈）/二氧化钛复合粒子（P(MMA-co-AN)/TiO2 复合粒子），希望通过引入强极性的－CN 和－COOCH3&nbs...
http://www.polymer.cn/research/dis_info5211 |
| |
P(St-co-M12-co-BPMA)/TiO2复合粒子抗紫外光性能研究
关键字：乳液聚合，复合粒子，抗紫外光性能
本文以苯乙烯（St）、反应型乳化剂M12、反应型紫外光吸收剂BPMA 和改性TiO2 为原料，通过乳液聚合，制备了P(St-co-M12-co-BPMA)/TiO2 复合粒子；通过紫外-可见漫反射光谱分析、差示扫描量热分析和失重分析等，研究了复合粒子的抗紫外光性能，并将复合粒子与聚苯乙烯进行比较，结果表明：复合粒子在BPMA和TiO2 共同作用下能吸收210-400nm 之间90%以上的紫外光，经过500 小时紫外光辐照后，复合粒子的...
http://www.polymer.cn/research/dis_info4820 |
| |
无规Poly(St-co-MMA)纳米球的制备
关键字：无规共聚poly(St-co-MMA) 己内酰胺 自组装 纳米球
人们一直在努力提高制备纳米颗粒的技术，起先的制备方法多使用表面活性剂，而表面活性剂对材料的性能影响很大。后来人们开始在尝试一些无皂的制备法，比如利用嵌段共聚物的不同段的溶解性 . 有温度诱导的, 化学反应诱导的, 聚合物-聚合物配位诱导的, 以及微米相反转的.更有使用无规的离聚物制备纳米颗粒的。
http://www.polymer.cn/research/dis_info4381 |
| |
聚（己二酸丁酯-co-对苯二甲酸丁酯）的多晶结构及降解性为
关键字：聚（己二酸丁酯-co-对苯二甲酸丁酯）
聚己二酸丁酯是可降解的脂肪族聚脂，在其主链上引入芳香族聚脂链段，既可以提高其机械性能有不失其可降解性。
http://www.polymer.cn/research/dis_info2385 |
| |
Preparation and Characterization of Cationic Chitosan-modified Poly(D,L-lactide-co-glycolide) Copolymer Nanospheres Poly(D,L-lactide-co-glycolide) Copolymer Nanospheres
关键字：Preparation,Characterization,Cationic,Chitosan,modified,Poly,lactide,glycolide,Copolymer,Nanospheres,Poly,lactide,glycolide,Copolymer,Nanospheres,
Gene delivery using cationic polymers is one of the greatest challenges for inventing non-viral vector systems instead of virus-based vectors. Polylactide (PLA), polyglycolide (PGA) and their copolymers (PLGA) have been demonstrated to be&n...
http://www.polymer.cn/research/dis_info1933 |
| |
Fe-Cr-Co合金高温磁稳定性研究
关键字：Fe-Cr-Co合金 磁稳定性 显微组织 穆斯堡尔谱
对Fe-Cr-Co合金在高温条件下的磁稳定性进行了研究。稳定性试验结果表明，（BH）max的不可逆变化率为Br和Hc的2～5倍，材料的磁性能，特别是（BH）max在开始阶段有一定的波动，随时间延长波动逐渐减小,经过稳定化处理的试样其稳定性有一定的改善。以单畴粒子理论为基础，讨论了各因素对磁性能的影响。透射电镜观察表明，合金的显微组织结构在稳定性试验前后没有发生明显的变化。穆斯堡尔谱分析发现，经过高温稳定性试验后，合金中的...
http://www.polymer.cn/research/dis_info975 |
| |
直接还原碳化法制备纳米复合WC-Co粉末
关键字：直接还原碳化 WC-Co 纳米复合
用直接还原碳化法制备了纳米复合WC-Co粉末。根据X射线衍射图研究了直接还原碳化温度及时间对反应产物的影响，用扫描电镜观察了粉末颗粒形貌和粒度分布。结果表明：用直接还原碳化法在950℃碳化4h可以得到100~300 nm、无η相的WC-Co复合粉末，该法具有碳化温度低、碳含量容易控制、适合工业化生产的优点。