Halogen-free flame retardant poly (vinyl alcohol) foams prepared through thermal processing
作者:Dan Guo, Shibing Bai, Qi Wang
关键字:Halogen-free flame retardant foams, Poly (vinyl alcohol) foams, Extrusion foaming
论文来源:会议
发表时间:2012年
Novel halogen-free flame retardant PVA-based composite foams were successfully prepared through continuous extrusion foaming using water as plasticizer and blowing agent. The morphology, cellular structure and flame retardancy of the prepared PVA foams were investigated. It was found that the halogen-free flame retardant containing nitrogen-phosphorus (NPCs) were well dispersed in PVA matrix due to the strong interactions between the amino and hydroxyl groups containing NCP molecules and the hydroxyl groups containing PVA molecules. The fine NCPs particles also acted as a good heterogeneous nucleating agent for foaming. Combustion test showed that the prepared PVA foams had excellent flame retardancy, its limiting oxygen index (LOI) reached up to 35% and passed the UL94 V-0 rating test, and compared to the control sample, its peak heat release rate (PHRR) declined, the temperature at the maximum peak heat release rate (TP) shifted to higher temperature. Both FT-IR and XPS analyses of the residual chars demonstrated that the catalytic effect and chemical reactivity of the NPCs during the chars forming reactions improved the flame retardancy of PVA foams.