Hydrothermally prepared nanosized and mesoporous Ce0.4Zr0.6O2 solid solutions with shape dependence in photocatalysis for the degradation of methylene blue
作者:Tian, W (Tian, Wei)[ 1 ] ; Yin, J (Yin, Jun)[ 2 ] ; Wei, LF (Wei, Lingfei)[ 1 ] ; Shen, QH (Shen, Qu
关键字:VISIBLE-LIGHT IRRADIATION; LAYERED CARBON NITRIDE; HYDROGEN-PRODUCTION; EFFICIENT DEGRADATION; SUPPORTED CATALYSTS; SOOT OXIDATION; H-2 EVOLUTION; CEO2 NANORODS; CONVERSION; COMPOSITE
论文来源:期刊
具体来源:RSC ADVANCES
发表时间:2017年

Mesoporous Ce0.4Zr0.6O2 solid solutions with four different shapes, including mixed nanorod and nanoparticle (RP, cubic), nanopolyhedron (PH, tetragonal), nanosphere (SP, cubic) and nanoegg (EG, tetragonal), were hydrothermally fabricated. Various physical and chemical techniqueswere used to reveal shape-dependent structural, optical, electronic andsurface properties, providing a powerful insight into the morphological dependence of photocatalytic activity towards methylene blue (MB) degradation. Among these samples, RP, consisting of a cubic Ce-rich phase (Ce0.6Zr0.4O2 nanorods) and a tetragonal Zr-rich phase (Ce0.2Zr0.8O2 nanoparticles), affords the optimal functionality, with a top degradation rate (D = 70.5%) and a peak rate constant (k = 0.0102 min(-1)). This occurrence results mainly from the prompt separation of excitons and suitable textural properties for MB absorption and activation. A brief introduction to the reaction path when using RP is proposed.