作者：Yin, J (Yin, Jun)[ 1 ] ; Zhou, JC (Zhou, Jiancheng)[ 1 ]
关键字：Organic-inorganic hybrid membranes; Si-ARGET ATRP; Hydrophilization; Antifouling; SiO2-g-(PDMAEMA-co-PDMAPS) NPs
论文来源：期刊
具体来源：DESALINATION
发表时间：2015年

To avoid the agglomeration of nanoparticles (NPs) in hybrid membranesand alleviate the leakage of NPs duringthe oily wastewater treatment process,poly(2-(dimethylamino)ethylmethacrylate co-3-dimethyl(methacryloyloxyethyl)ammoniumpropanesulfonate)(PDMAEMA-co-PDMAPS) grafted silica (SiO2) [SiO2-g-(PDMAEMA-co-PDMAPS)]NPs were prepared by grafting PDMAEMA brushes onto SiO2 NPs surface via the-surface-initiated activators regenerated by electron transfer atom transfer radical polymerization (Si-ARGET ATRP). Subsequently, Thequatemization of the tertiary amine groups in PDMAEMA and 1,3-propanesultone was performed to get [SiO2-g-(PDMAEMA-co-PDMAPS)] NPs. Then, the organic-inorganic hybrid polyethersulfone (PES) membranes with different ratios of SiO2 NPs (m membranes) and SiO2-g-(PDMAEMA-co-PDMAPS) NPs (M membranes) were fabricated via the non-solvent induced phase separation (NIPS) process. Transmission electron microscopy (TEM) images demonstrated that the modification of SiO2 NPs with PDMAEMA-co-PDMAPS was favorable for their homogeneous dispersion in organic solvents. The results of scanning electron microscopy (SEM) images indicated that the surface porosity and mean pore size of hybrid membranes were increased compared to the neat PES membrane. Furthermore, the M membranes exhibited better hydrophilicity, pure water flux and oil flux than neat PES membrane and m membranes. It was found from filtration results that the total fouling (R-t) and irreversible fouling (R-ir) were significantly reduced due to higher hydrophilicity of hybrid membranes. In addition, after oil-in-water emulsion filtration, M membranes exhibited higher water flux recovery

ratio (FRR) value than that of m membranes and neat PES membrane. (C) 2015 Elsevier B.V. All rights reserved.