作者：Fang F, Song PA, Ran SY, Guo ZH, Wang H, Fang ZP*
关键字：Epoxy resin; Self-assembled supermolecular aggregate; P, N-containing flame retardants; Graphene; Flame retardancy
论文来源：期刊
具体来源：Composites Communications, 2018.8, 10: 97-102
发表时间：2018年
In this paper, we have reported a facile way to functionalize graphene oxide (GO) via assembling a supermolecular aggregate of piperazine (PiP) and phytic acid (PA) onto the GO surface (PPGO) without using any organic solvent. The functionalization of GO is confirmed by the X-ray photoelectron spectrum (XPS), transmission electron micrographs (TEM) and Raman spectrum. The introduction of 3 wt% PPGO into epoxy resin (EP/PPGO3) results in notable suppression on the fire risk of epoxy resin. In addition, cone calorimeter tests showed that the peak heat release rate (pHRR) was decreased from 727.4 kW/m2 to 367.5 kW/m2 (49%), and the peak smoke production rate (pSPR) was decreased from 0.2316 m2/s to 0.1379 g/s (40%). The improved flame-retardant performance of EP nanocomposites is most likely due to a tripartite cooperative effect from the key components (piperizine, phytic acid, and GO). This strategy demonstrates a facile and efficient approach for fabricating highly effective graphene-based flame retardants for polymers.