    高平教授在纳米防皱纺织品研究领域也颇有建树。她与徐兵教授的研究小组研发成功一种应用于纳米颗粒材料对纺织品进行防皱处理的新技术。目前商用的纺织品防皱处理常常会损坏织物的强度，而新发明的纳米防皱处理技术在达到防皱效果的同时，可有效保持纺织品固有的强度。该研究小组已掌握大规模生产纳米防皱处理所需的纳米颗粒材料的方法，而该技术的生产成本已低至商业应用可接受的水平。该技术除可广泛应用于各类纺织品的防皱处理，还可用于纸张的防皱处理。目前，该研究人员已就相关技术申请专利并与本地的一家纺织厂合作开发相关产品。
主要研究成果：

(1)Invented the strongest fiber for ballistic proof vests.  Supported by DSM and Hong Kong government (RGC) Grant, we successfully spun UHMWPE fibers containing 5 wt% CNTs to produce fibers with tensile strength greater than 4.2 GPa and Young’s modulus greater than 135 GPa.  (See our paper published in 2006 in Polymer).
(2)We have developed a novel self-humidfying Nafion nanocomposite membrane for fuel cell applications.  The membrane shows an enhancement of power density of 170% in comparison with the commercial membrane when used with hydration. (see our 2008 paper in Langmuir).
(3)We have developed a liquid crystalline polymer which can reduce the bulk viscosity reduction up to 95% in HDPE at 1 wt% TLCP loadings. (see our 2005 papers in Polymer.

参与课题：
时间： 2005-2003
课题题目：利用纳米技术提高棉质纺织品的耐久压烫性。
课题描述：免烫棉质纺织品容易整理而深受消费者喜爱。然而，由于内部纤维的交联作用导致棉质纺织品的柔软性不够，其拉伸强度、撕裂强度和耐磨性分别降低了40%，60%，50%，这意味着棉质纺织品易破损和耐磨性差。这些力学性能的降低限制了免烫棉质纺织品在高端面料的应用。如今纳米技术在解决这个问题上可以发挥重要作用。通过纳米涂层的机械强度可以增强棉质纺织品的力学强度，同时保持令人满意的抗皱性。此课题的研究方向是设计最优配比的纳米颗粒和织物处理工艺，同时乳液合成技术和织物处理工艺达到工业生产水准。